Jan 19, 2024

Preparation and characterization of low

Scientific Reports volume 13, Article number: 4493 (2023) Cite this article 1661 Accesses 1 Citations Metrics details Malachite green used in textile and dyeing industries is a common persistent

Scientific Reports volume 13, Article number: 4493 (2023) Cite this article

1661 Accesses

1 Citations

Metrics details

Malachite green used in textile and dyeing industries is a common persistent pollutant in wastewater and the environment causing major hazards to human health and aquatic organisms. In this study, the response surface methodology was applied to optimize the adsorptive removal of malachite green using nano-bentonite, MgO-impregnated clay, and Mucor sp. composites. The nano materials and Mucor sp. composite were characterized by FTIR, SEM and X-ray diffractometry. According to the obtained results, nano-bentonite exhibits a maximum MG adsorption efficiency of 98.6% at 35 °C, pH 7.0, 60 min contact time, 1.0 g/L adsorbent dosage, and 50 mg/L initial MG concentration. On the other hand, the maximum efficiency for MG adsorption on MgO-impregnated clay of 97.04% is observed at pH 9.0, 60 min contact time, 0.7 g/L adsorbent dosage, and 50 mg/L initial MG concentration. The Malachite green (MG) adsorption isotherm on MgO-impregnated clay corresponded with the Freundlich isotherm, with a correlation coefficient (R2) of 0.982. However, the Langmuir adsorption isotherm was a superior fit for nano-bentonite (R2 = 0.992). The adsorption activities of nano-bentonite and MgO-impregnated clay were fitted into a pseudo-second-order kinetic model with R2 of 0.996 and 0.995, respectively. Additionally, despite being recycled numerous times, the adsorbent maintained its high structural stability and removal effectiveness for nano-bentonite (94.5–86%) and MgO-impregnated clay (92–83%).

Water pollution caused by wastewater from textile manufacturing activities is a major global concern. One of the most difficult tasks that researchers are faced with around the world in the twenty-first century is to provide the clean water necessary for industrial, house hold, and agricultural activities1. Textile factories are responsible for one of the major environmental pollution issues in the world, because they discharge undesirable dye effluents2. The textile industry consumes 100–200 L of water per kg of textiles produced, resulting in the generation of large amounts of wastewater during the dyeing process3. Globally, about 280,000 tons of synthetic dyes are discharged into natural streams every year from wastewater produced by a variety industries, such as leather, food, textile, paper, cosmetic, printing, and carpet manufacturers4. The said discharge has an adverse impact on the visual quality of water bodies, and it interferes with the lifecycles of aquatic organisms by reducing the penetration of sunlight into the water, which inhibits photosynthesis and plant growth, thereby affecting the biological activity of aquatic animals; moreover, the synthetic dyes present in water bodies also cause soil contamination5. Malachite green (MG) is a synthetic dye used to dye silk, cotton, leather, wool, and paper, and it is also employed as a fungicide and disinfectant in the fish farming industry, as it affords the control of fish parasites and diseases6. MG is a cationic triphenylmethane compound that is highly soluble in water7. It is also highly toxic to mammalian cells at concentrations below 0.1 g/mL8. MG is characterized by a complex molecular structure, high stability, non-biodegradability, and high resistance to light and oxidizing agents7. When it flows into the receiving stream, this dye negatively affects the lifecycles of aquatic organisms by interfering with the physiology of the pituitary liver, gills, kidneys, intestines, gonads, and gonad vegetative cells9. In humans, MG inhalation can cause inflammation of the respiratory tract, while its swallowing can cause inflammation of the digestive tract10. MG is hazardous to humans, and mutagenic; additionally, its presence affects the immunological and reproductive systems11. Malachite green can be converted into leucoMalachite green and carbinol, which is toxic to humans. In fish muscles, fat, and internal organs, MG has a half-life of 10 days12. This cationic dye is also durable in the environment, with a half-life of 12.9–50.34 days in sediment13. Many technologies have been used to treat textile wastewater, including physical, chemical, and advanced treatment methods, such as membrane filtration, ion exchange, electrochemical technology, coagulation, flocculation, reverse osmosis, chemical oxidation, ozonation14, and biological treatment for fungi and bacteria effects15. However, most of these technologies have various disadvantages, including low efficiency, large capital investment, high energy consumption, high cost, non-selectiveness, unsuitability for large-scale applications, and the formation of harmful secondary sludge16. Among the treatment strategies, adsorption is one of the most appealing and efficient methods for removing dyes from polluted water samples. This technique provides various advantages, including a simple design, recyclable adsorbents, simple operation, non toxicity, low cost, and a modest initial investment17. These recyclable adsorbents include activated carbon (AC)18, lime peel19, and pumice20. However, there are various downsides to the different adsorbents used to purify water. For example, reusing AC requires regeneration, which is costly and limits its large-scale application in wastewater treatment. In addition, some adsorbents are effective against a limited number of dyes and are difficult to separate from treated water21. Reference22 focused on the immobilization of horseradish peroxidase onto supports such as polyamide-6 electrospun fibers, which were used for the decolorization of reactive black 5 and malachite green textile dyes from solutions imitating polluted sea waters and reached over 70%. Reference23 presented the application of immobilization of laccase from Trichoderma versicolor onto various supports, such as TiO2–ZrO2–SiO2, to remove the azo dye reactive black 5 (RB5), the anthraquinone dye reactive blue 4 (RB4), degradation efficiencies reaching 100%, 91%, and 77%, respectively, they gained over 70% catalytic activity of immobilized laccase on TiO2–ZrO2–SiO2 even after five run cycles. Recently, scientists have developed an efficient and economical adsorbent material, nano-clay polymer composites, to overcome the shortcomings of traditional purification methods for textile industry wastewater and reduce their environmental threat. Currently, clay is widely used in various industries, including cosmetics, oil exploration, pharmaceuticals, food, and papermaking, because it is easily available, nontoxic, and has the potential for ion exchange for the removal of dyes from wastewater24. Among the clay materials studied, bentonite has received considerable attention as an adsorbent due to its low cost, renewability, large surface area, good chemical and mechanical stability, and abundance in nature25. Furthermore, bentonite is mostly composed of montmorillonite26. Raw bentonite has poor adsorption capacity for cationic dyes, so it is modified using physical and chemical treatments. However, the negatively charged surface lattice of bentonite clay may have a superior absorption capacity for cationic dyes27. Chemically treated modified bentonite has been used to remove cationic basic methylene blue28, metal ions29, and crystal violet30. Thus, this study aims to evaluate the effectiveness of modeling of the response surface methodology, which was analyzed during the experiments to optimize and assess the interactive effects of nano-bentonite, MgO-impregnated clay, and Mucor sp. on MG removal. Furthermore, isotherms, pseudo-first-order and pseudo-second-order models and thermodynamic parameters were determined.

The bentonite used in this study was obtained from CMB Co. (Egypt). Magnesium chloride dihydrate (MgCl2·2H2O) and hydrochloric acid were provided by Sigma-Aldrich Co. (Egypt).

Magnesium-impregnated clay and nano-bentonite were characterized by scanning electron microscopy (SEM) (Quanta 250 FEI Company), transmission electron microscopy (TEM) with a JEOL-JEM-2100, Fourier-transform infrared (FTIR) spectroscopy analysis performed with a Bruker-VERTEX 80 V instrument ranging from 900 to 5 cm−1 wavenumber range, and X-Ray diffractometry (XRD) with a PANalytical X’Pert Pro(United Kingdom).

The cationic dye MG (Fig. 1; chemical formula: C46H50N42C2HO4C2H204, MW: 927.1 g/mol) was purchased from MERCK Pvt. Ltd(England). A 1 g sample of the appropriate MG was dissolved in 1000 mL of distilled water to produce an MG stock solution of 1000 mg/L concentration. The stock solution was then used to prepare MG solutions of concentrations ranging from 30 to 150 mg/L. The initial pH of the stock solution was adjusted by adding to it 0.1 M HCl or NaOH. A 50 ml aliquot of the MG stock solution was used for each of the experiments. All experiments were conducted in triplicate.

Molecular structure of Malachite green.

An amount of 21 g of bentonite powder and 100 mL of12 M HCl solution were combined, and the resulting mixture was heated in a magnetic stirrer at around 343 K and stirred at a rate of 340 rpm for 120 min. Subsequently, the obtained suspension was filtered and the precipitate was repeatedly washed with distilled water until the pH of the water used to wash the residue reached neutrality. The thus obtained acid-activated bentonite was dried in the oven for 5 h at a temperature of 373 K. The precipitate was then ground in a mortar to produce a powder, which was calcined in a furnace at 600 °C for 2 h31.

A mixture of 7 g of bentonite clay and 100 mL of 1.25 M magnesium chloride solution was stirred for 6 h. After stirring; the solution was poured into a glass petri dish and dried in an oven at 150 °C. The dried mixture was crushed to a fine powder and calcined in a muffle furnace at 450 °C for 2 h. The calcined powder was cooled, washed twice with deionized water, and dried at 70 °C for 6 h32.

The pH point of zero surface charge characteristics of nano-bentonite and MgO-impregnated clay was determined using the following method33: 50 mL of 0.1 M NaCl solution was transferred into 100 mL Erlenmeyer flasks, with the initial pH (pHi) values adjusted from 3.0 to 12.0 by adding 0.1 M HCl or NaOH. Next, 0.3 g nano-bentonite and MgO-impregnated clay were added to each flask, and the suspensions were stirred continuously for 24 h. The final pH values of the supernatant liquids were assessed after 24 h. The pH PZC was plotted against the difference between the initial and final pH (pHf) values. The zero point of charge (pHZPC) of the substance was considered the point where the resulting curve intersected the pHi axis at pH = 0.

Batch adsorption experiments were carried out to achieve the optimum operating conditions for removing of the MG dye. 100 mL solution of dye initial concentration was taken in 250 mL flasks and a known amount of nano-bentonite and MgO-impregnated clay, the adsorbents were added to the solutions. The mixture was shaken mechanically at a constant speed of 200 rpm using rotary shaker (Dragon LAB, skp-0330-pro, Germany).

The effects that different experimental parameters had on the efficiency of MG removal were investigated. In particular, various values were utilized for the pH (3.0, 5.0, 6.0, 7.0, 8.0, 9.0, 10.0, and 11.0), contact time (10–60 min), adsorbent dosage (0.05, 0.1, 0.2, 0.5, 0.7, and 1.0 g/L), initial dye concentration (50–250 mg/L), and temperature (298, 303, 323, and 343 K). The initial pH values were adjusted using 0.1 M HCl or 0.1 M NaOH solutions and a pH meter (Multi 9620 IDS-pH meter, WTW, Germany). Each experiment was performed three times and the averages values of the measurable were calculated and presented. Samples were taken out after the equilibrium time (60 min) and centrifuged at 4000 rpm for 25 min to completely separate the nanobentonite and MgO-impregnated clay from the solution and MG concentrations in the supernatants were determined measuring the supernatants’ absorption at the wavelength at which MG exhibits its maximum absorption (λmax = 620 nm) using a spectrophotometer (Thermo Fisher Scientific, Orion Aquamat 8000, USA). MG removal efficiency, R (%), was determined through Eq. (1):

where C0 and Cf represent the initial and final concentrations of the dye solution (mg/L).

The adsorption capacity (qe, mg/g) at equilibrium, was determined using Eq. (2):

where Ci (mg/L) and Ce (mg/L) are the MG dye concentrations in the initial solution and at equilibrium, respectively; V (L) is the volume of the solution; and w is the mass of the adsorbent (mg).

In the current investigation, the equilibrium condition for the adsorption of MG on nano-bentonite and MgO-impregnated clay was described using the Langmuir, Freundlich, and Tempkin models, as given by34.

Pseudo-first-order and pseudo-second-order kinetic models were utilized to analyze the kinetics of MG adsorption on the adsorbents. The pseudo-primary-order model, in its linear form is described by35.

As a design method, the response surface methodology (RSM) is a mathematical tool that uses a second-order equation to determine the best conditions between the controllable input factors and the response variable. The effects of various factors, such as pH (X1), temperature (X2), adsorbent dosage (X3), and initial concentration (X4), on the decolorization process, were studied using the Box–Behnken design. Twenty-seven experimental runs were obtained according to the three levels of each variable; low level (− 1), level; (0) (medium) and high level (1) were used to design and analyze the experiments (Table 1). The second-order quadratic equation model was assessed to predict the optimum value between the dependent and independent factors. The correlation’s general form can be stated according to Eq. (3):

Here, Y is the predicted response factor (the removal of MG), and X is the input variable. β0, βj, βjj, and βij are the intercept, linear effect, square effect, and interaction effect, respectively. N is the quantity of input-controlling coded variable. The coefficient of determination (R2) and Fisher’s F-test were used to describe the quality of the quadratic model equation. Using Design-Expert 13, an analysis of variance (ANOVA) was conducted to determine the model’s statistical significance.

The microbial toxicity of the Malachite green dye on Escherichia coli, Staphylococcus aureus, and Pseudomonas aeruginose was investigated. Furthermore, using an agar well assay, the toxicity of the dye and its breakdown products were investigated. After 24 h of incubation at 37 °C, the zone of microbial growth inhibition was recorded.

A pure fungal strain was isolated from wastewater, and seven fungal strains capable of decolorizing the Malachite green dye were identified. The ability of the fungal strain to decolorize the dye was carried out in Sabroud dextrose broth SDB amended with Malachite green dye (5 mg/L). The Erlenmeyer flasks contained 100 mL sterile media with dye and were inoculated with an immobilized fungal strain. The flasks were placed in an incubator shaker for 72 h at 30 ± 2 °C. The samples were withdrawn aseptically at 24, 30, 36, 48, and 72 h alternately and centrifuged at 4500 rpm for 10 min. Furthermore, the supernatant was scanned in a spectrophotometer at λmax (620 nm) of Malachite green dye. The control flasks underwent similar former conditions, but without fungal biomass. Among the isolated strains, Mucor sp. optimally decolorized Malachite green, with a removal efficiency of 92.2%. The resultant sequence was given to the National Center for Biotechnology Information (NCBI), where it was assigned an accession number (ON934589.1). Figure 2 shows that the gene sequence was examined using NCBI’s Basic Local Alignment Search Tool (BLAST) and that a phylogenetic tree was formed using Mega 7.0.

Phylogenetic tree of the fungal isolate Mucor sp.

A sodium alginate stock solution prepared using 2 g of sodium alginate (R&M Chemicals) was dissolved in 50 mL of distilled water. Separately, bentonite was made by dissolving 1 g of bentonite and 1 g of active carbon in 50 mL of distilled water and stirring the mixture to create a homogeneous suspension. Afterward, the bentonite solution and alginate were combined and autoclaved for 20 min at 121 °C. A total of 10 g pellets of fungal cells were obtained through centrifugation (46,000 rpm for 21 min) after they were cultured in Sabroud dextrose broth. They were then combined with alginate (2% by weight) and bentonite (1% by weight) and dropped separately into 100 mL of CaCl2 solution (3% by weight) with continuous stirring. The beads formed were left for 1 h at 37 °C, washed thoroughly in distilled water, and stored for 24 h at 4 °C.

The Box–Behnken design was used to examine the effects of four significant variables on the decolorization of MG by immobilized Mucor sp. These variables included pH (5–9) (A), temperature (25–45 °C) (B), fungal concentration (1.0, 2.0, and 3.0 g), contact time (24–72 h) (C), and initial concentrations (5–200 mg/L) (D). Flasks were kept in an incubator shaker at 120 rpm, and the optical density at λmax (620 nm) was recorded to determine the concentration of MG in the supernatant.

Data were analyzed using a variety of statistical techniques, including the root mean square error (RMSE), which was calculated according to Eq. (4), where n and p are the number of experimental data and parameters number of the model, respectively. Where Pdi and Obi are predicted values and experimental data, respectively. The models for describing the maximum growth rate of Mucor sp. were evaluated using both the bias factor (Bf) and the accuracy factor (Af), as calculated according to Eqs. (5) and (6). A model is considered fail-safe if its Bf value is more than 1.0 and fail-dangerous if its Bf value is less than 1.0. On the other hand, the value of Af is never larger than 1.0, with accurate models being characterized by values for this parameter that are close to 1.0. The Akaike information criterion (AIC) is a measure of the relative quality of mathematical analyses for a given set of data, and a criterion for error prediction was calculated according to Eq. (7). The R2 formula is modified for nonlinear models to incorporate the residual mean squared error and S2y, which is the total variance of the Y-variable36.

An XRD analysis (Fig. 3a) was conducted to determine the mineralogical constitution and crystalline nature of the nano-bentonite sample. The intensities of the XRD peaks were relatively high, which is an indication of high crystallinity. Based on the XRD pattern, we can conclude that Kaolinite-1A and quartz were the major constituents of modified bentonite, a conclusion confirmed by standard data for bentonite (ref’s: 01-075-8320 and 00-058-2028). The dominant diffraction peaks for nano-bentonite were found at values for Bragg’s angle (2θ) of ~ 12.2°,20.79°, 26.60°, ~ 27.3°, 34.88°, and. 39.43°,which are due to the presence of kaolinite, and of 19.79°, 36.47°, 42.4303°, 45.7659°, and 50.107°,which are due to the presence of quartz. The decrease of the interlayer space of nano bentonite indicates that some molecules of MG were adsorbed on top of the layers, a phenomenon that may be due to an electrostatic interaction between the positively charged groups of dye surfactant molecules with the negatively charged surface sites of nano-bentonite37,38. Scherrer's Eq. (10) has been used to calculate the crystallites' size (D):

where D is the crystallite size, β is the full width at half maximum, λ is the X-ray wavelength, and θ is Bragg’s angle. The estimated size of the average nano-bentonite crystallite was ~ 38 nm. In Fig. 3b are reported the XRD patterns of MgO-impregnated clay. According to this figure, the said clay sample exhibited various peaks of different intensities. Indeed, peaks were observed at 2θ values of 20.91°, 26.61°, 36.57°, 37.63°, 50.14°, 56.72°, 12.27°, 18.60°, 58.76°, and 42.8392°, indicating the presence in the sample of quartzite (40%), kaolinite (10%), and MgO nanoparticles (50%), respectively. The average crystallite size was estimated to be ~ 46.6 nm. The peaks in the XRD pattern of MgO-impregnated clay generally vanished and were reduced in size, and the clay's structure changed from crystalline to slightly amorphous, demonstrating the occurrence of chemisorption processes3.

(a) Nano bentonite and (b) MgO impregnated clay XRD chromatogram after adsorption.

The broad infrared spectroscopy bond-stretching peak between 3693.93 and 1630.21 cm−1 wave numbers (Fig. 4a) is indicative of the presence of OH stretching in hydration water on the bentonite surface. Notably, in Ref.39 detected peaks on the bentonite surface at 3450 and 1650 cm−1 wave numbers, which confirmed the existence of OH groups. In the FTIR spectra recorded in the present study. The stretching vibration of the Si–O bond was detected as avery strong absorption band at 1006 cm−1, providing strong evidence of the presence of a silicate structure. Due to the electrostatic attraction between the bentonite Si–O groups and the MG's positively charged moiety, and it indicates that the Si–O groups of bentonite may be involved in the process of dye adsorption, while the shift in the wave number values of the peaks indicates that substrate adsorption did indeed occur40. The peak at 920.80 cm−1 is attributed to the bending vibration of Al–OH–Al groups41. The presence of quartz in bentonite may be inferred from the peaks at 795 and 533 cm−1. According to42, the presence of quartz is confirmed by a band appearing at 796 cm−1. Reference43 attribute the bands at 500–400 cm−1 wave numbers to the bending vibrations of the Al–O–Si (octahedral Al) and Si–O–Si (tetrahedral Si) groups. The FTIR spectrum of the species obtained after MgO-impregnated clay underwent MG adsorption is reported in Fig. 4b. The bands at 3861 and 3622 cm−1 correspond to the stretching vibrations of the O–H bond of Si–OH groups coordinated to two Al atoms, whereas the band at 3207 cm−1 is due to MG captured by MgO. The band at 1641 cm−1 is due to the bending of water molecules, and the peak at 1423 cm−1 is attributed to the Si–O bond vibration mode. The deep band at around 1040 cm−1 is due to the stretching of the Si–O bond in the Si–O–Si groups of the tetrahedral sheet. The peak at 913 cm−1 is due to the deformation of the Al–Al–OH group; indeed, this peak is very close in position to the peaks at 913 and 914 cm−1 reported by Ref.44.The FTIR peaks appearing at 800 and 620 cm−1 are associated with Al–O + Si–O bending vibrations, while the peak at 537 cm−1 is associated with the bending vibration of the Al–O–Si group, and their observation is indicative of the presence of crystalline quartz.

FTIR Images of nano bentonite (a) and (b) MgO impregnated into clay after MG adsorption.

As can be evinced from Fig. 5a,b, the TEM images of nano-bentonite and MgO-impregnated clay indicated that these samples were irregularly shaped, heterogeneous, and semi-spherical. The surface morphologies of nano-bentonite and MgO-impregnated clay were investigated by SEM (see Fig. 5c,d, respectively). Nano-bentonite was observed to have a smooth surface and an irregular shape while surface morphology reveals a spongy appearance with an uneven structure. Additionally, micrographs of the MgO-impregnated clay powder indicate the presence of huge agglomerates of extremely fine MgO particles; these data also suggest that the said powder is highly porous. The generation of pores and voids may be caused by the bentonite clay swelling upon treatment with magnesium salt, which, upon desiccation and calcination, results in the formation of MgO clusters in the interlayer spaces of bentonite. At various magnifications, secondary electron images were acquired in order to study their morphologies and elemental compositions. The SEM image of the nano-bentonite and MgO-impregnated clay after adsorption of MG dye shows that the surface of the adsorbent is rough with an increased number of voids, as shown in Fig. 5e,f, respectively. The average crystallite sizes of MgO-impregnated clay and nano-bentonite, which were estimated via the Debye–Scherrer equation, were 46.6 and 38.9 nm, respectively, and were found to be close to the average particle size computed from individual particles: 43.2 and 34 nm, for MgO-impregnated clay and nano-bentonite, respectively. Figure 5g displays the surface morphologies of the fungus hyphae and active carbon after they have absorbed the MG. The outer surface of the fungal biomass and active carbon (AC) are coated with particles with diameters ranging from 0.1 to 1 mm, suggesting that the dyes were primarily adsorbable onto the fungus hyphae and AC. The presence of polysaccharides in the fungal biomass cell wall gives the hyphae ball a great capacity for biosorption45.

TEM (a) nano bentonite, (b) MgO impregnated clay, and SEM images and Energy dispersive X-ray analysis (c) nano bentonite within EDX, (d) MgO impregnated clay within EDX (e) nano bentonite after adsorption MG, (f) MgO impregnated clay after adsorption MG and (g) after adsorption MG by fungi low and high magnification respectively.

According to several studies, the initial pH of a solution is one of the most important environmental factors influencing the adsorption process, because it affects adsorbate solubility and surface charge, as well as adsorbate speciation and degree of ionization. The effect of the initial pH on the capacity of nano-bentonite and MgO-impregnated clay to adsorb MG was investigated over the 3.0–11.0 pH range. In Fig. 6 are reported data reflecting the influence that the initial pH had on dye removal, in conditions where by the initial concentration of the dye (50 mg/L), the contact time (60 min), the temperature (35 °C), and adsorbent dosage(1.0 g) were kept constant. As can be evinced from Fig. 6, MgO-impregnated clay exhibited good adsorption, with the maximum percent removal of MG (97.04%) observed at pH 9.0.On the other hand, the maximum uptake of MG by nano-bentonite reached a value of 99.8% at pH7.0. The values for the zero point charge (pHzpc) of nano-bentonite and MgO-impregnated clay were found to be 5.5 and 7.1, respectively. Thus, at pHzpc (5.5 and 7.1, respectively), the nano-bentonite and MgO-impregnated clay had net positive surface charge and negative surface charge at pH > pHpzc. The low adsorption capacity exhibited by the two species under acidic conditions could be mainly attributed to the decrease in the number of negative charges on the adsorbents’ surfaces and the increase in the number of positively charged sites in the adsorbents, which can cause electrostatic repulsion between the adsorbent and the dye molecules; moreover, the presence of excess amounts of H+ ions may result in the said ions competing with the cationic MG species for adsorption onto nano-bentonite and MgO-impregnated clay. As a consequence, the probability of MG molecules being adsorbed on the two adsorbents may decrease. By contrast, as the pH increased, the deprotonation of the acid sites on the surface of nano-bentonite and MgO-impregnated clay composites resulted in the number of negatively charged adsorbent sites to increase46. According to Ref.47, who examined the relationship between pH and the adsorption of MG onto bentonite, the interactions between the cationic amine moiety of MG and the negatively charged SiO2 in the bentonite. The cationic active sites are present and exhibit an increased likelihood of binding MG when the pH of the solution is between 5 and 6. As a result of the strong electrostatic interactions between MG and the adsorbents, the surface diffusion of the dye molecules increases. Similar conclusions were reached by Ref.30,who attributed the increase in adsorption observed as the pH increased to a reduction in the competition for functional groups between the target cations and the protons present in solution. Our findings paralleled those of Ref.48, who discovered that the removal of MG dye by titanium coated graphite was lowest at pH 3.0 (56.2%) and highest at pH 7 (95%). Our results are consistent with those reported in Ref.17 at pH 7, the Shell's seeds of Ziziphus spina christi adsorbed 91.1% of Malachite green dye.

Effect of pH on MG dye removal by (a) nano bentonite and (b) MgO impregnated clay.

One of the factors that was observed to affect MG adsorption is the temperature. The effect of temperature on dye discoloration was evaluated preparing a mixture of MG with nano-bentonite or MgO-impregnated clay at different temperatures in the 25 °C–70 °C range, while keeping the adsorbent dosage (0.7 g), the pH (7), the contact time (60 min), and agitation speed (200 rpm) constant. As can be evinced from Fig. 7, evidence indicates that the rate of adsorption of MG onto nano-bentonite increased as the temperature was raised from 25 to 35 °C; the said rate of MG adsorption then gradually decreased as the temperature rose above 40 °C, an observation that may be attributed to the bonds between the dye molecules and the active sites of the adsorbents getting weakened. At 25 °C, the percentage removal of MG was 92.2%; at 35 °C, this parameter increased to 99.8%; past the said temperature mark, the percent MG removal did not display any significant change until the temperature reached 70 °C.This evidence indicates that the adsorption process was slightly endothermic. A similar trend was reported by Ref.28 for the removal methylene blue by activated bentonite. On the other hand, the percent removal of MG by MgO-impregnated clay increased when the temperature was raised from 25 to 70 °C. At 25 °C, the percentage removal of the dye was 88.3%; at 70 °C, this value increased to 99.7%. The adsorption process was exothermic, as shown in Fig. 7. Indeed, the increase in percentage removal is observed because the kinetic energy of the molecules increases as the temperature increases, and the accelerated molecules disperse faster in the adsorbent49. In addition, the increased temperature will cause the internal structure of the adsorbent to swell, allowing large dyes to penetrate the adsorbent50. This finding was consistent with the data reported by Saleh Bashanaini17, who found that the value for MG removal with activated carbon prepared from shells seeds increased up to 95% as a result of the temperature being raised to 50 °C.

Effect of temperature on MG dye removal by (a) nano bentonite and (b) MgO impregnated clay.

Assessing the effect of the contact time is important because the results of such an investigation provide basic information on how quickly the adsorption process reaches equilibrium. The effect that changing the contact time in the 10–60 min range had on the adsorption capacity was studied while other parameters were kept constant (adsorbent dosage, 0.7 g; pH 7; initial MG concentration, 50 mg/L; agitation speed, 200 rpm; temperature, 35 °C). Based on the results reported in Fig. 8, rapid dye adsorption was observed in the initial phase of the experiment; subsequently, dye adsorption gradually slowed down, as the equilibrium condition was approached after about 60 min. In the case of nano-bentonite, at the 10 min mark, the percentage removal of MG was 90.9%, and the value for this parameter gradually increased to 95.3% at the 20 min mark and to 98.2% at the 60 min mark. In the case of the MgO-impregnated clay, the MG percentage removal was89.8% at the 10 min mark; it increased sharply to 95.9% at the 30 min mark, and to 96.8% at the 60 min mark. In fact, the maximum removal efficiency achieved by nano-bentonite was 98.2%, where as that achieved by MgO-impregnated clay was 96.8%.The time required to reach equilibrium in the adsorption of MG on nano-bentonite and on MgO-impregnated clay was found to be 30 min. The described trend could be rationalized by envisioning a situation where by MG molecules proceeded to occupy a large number of initially vacant active sites onthe surfaces of the adsorbents, resulting in a high initial adsorption rate; as the contact time increased, however, the MG adsorption rate decreased as the number of vacant sites decreased and the repulsive forces between the dye molecules adsorbed on the biomass increased, and the large phase led to a significant decrease in absorption capacity, so that the dye molecules slowly diffused into the interior of the adsorbents51. The results of the present study are consistent with those reported by Tarekegn and Balakrishnan3 on the effects of contact time on the adsorption of methylene blue dyes on nano-zero-valent iron, nano-clay, and iron-impregnated nano-clay52. Present study is consistent with previous literature3 who, reported that the effects of contact time on the adsorption of Malachite green dye on the titanium coated graphite with CNT-ABS adsorbents achieved removal efficiency at 35%, (20 min) and it increased to 97.3% at 60 min.

Effect of contact time on MG dye removal by (a) nano bentonite and (b) MgO impregnated clay.

The effect of the initial concentration of MG on nano-bentonite and MgO-impregnated clay was investigated by making the said concentration vary in the 50–250 mg/L, range, while the other parameters were kept constant (contact time, 60 min; pH 7; initial concentration, 50 mg/L; agitation speed, 200 rpm; temperature, 35 °C). The dye removal efficiency of the adsorbents declined as the initial concentration of MG increased. Notably, the dye adsorption activity of MgO-impregnated clay was less influenced by changes in the initial concentration of the adsorbate than nano-bentonite. The MG removal efficiency of MgO-impregnated clay declined from 96.7 to 89.7% as the initial MG concentration increased from50 to 250 mg/L (see Fig. 9). While nano-bentonite achieved a maximum MG removal efficiency of 98.6% at an initial concentration of MG of 50 mg/L, this parameter’s value was reduced to 91.5% when the initial concentration of MG increased to 250 mg/L. This trend can probably be explained considering that the lower the initial concentration of MG, the larger the proportion of initially vacant (available) active sites on the surface of the adsorbent. Fairly similar observations were reported by Ref.2,48. Our results were in agreement with the previous study by Ref.3, which found that the iron impregnated clay's ability to remove MB dye from 98.86 to 76.80% at doses of 20–80 mg/L, respectively.

Effect of initial MG dye concentration on MG dye removal by (a) nano bentonite and (b) MgO impregnated clay.

The dosage of nano-bentonite and MgO-impregnated clay was another crucial factor influencing dye adsorption activity. The dosages of nano-bentonite and MgO-impregnated clay were made to have the following values: 0.1, 0.2, 0.5, 0.7, and 1.0 g; in the experiments conducted, the initial MG concentration (50 mg/L), temperature (35 °C), agitation speed (200 r/min), and pH (7) were kept constant. As can be evinced from in Fig. 10, the dosages of nano-bentonite and MgO-impregnated clay that afforded the maximum rate of MG removal were 1.0 and 0.7 g, respectively. The maximum MG removal efficiency achieved by nano-bentonite was 98.6% and that achieved by MgO-impregnated clay was 97.4%. The MG adsorption rate of MgO-impregnated clay increased sharply from 48.1% measured at a 0.05 g dosage of MgO-impregnated clay to 97.8% at a 0.7 g dosage of the said adsorbent. The adsorption efficiency of MgO-impregnated clay then increased gradually to 98.1% at a 1.0 g dosage. By contrast, nano-bentonite exhibited a higher adsorption rate than MgO-impregnated clay at a 0.05 g dosage (67.1%) and a more gradual increase in adsorption efficiency as its dosage increased to 0.7 g (adsorption rate: 99.8%). The MG removal efficiency remained constant as the adsorbent dosage was made to increase further to 1.0 g (Fig. 10). The results of these experiments were consistent with those reported by Ref.53, which indicated that the initial concentration of MG was inversely proportional to the efficiency of MG adsorption on silver nanoparticles coated on activated carbon.

Effect of adsorbent dose on MG dye removal by (a) nano bentonite and (b) MgO impregnated clay.

In order to optimize the adsorption process, a Box–Behnken design with four factors (initial concentration of dye, temperature, adsorbent dose, and pH) was chosen. The higher and lower levels of the variables are listed in Table 1, while the experimental and predicted values of the percentage decolorization of MG in the presence of nano-bentonite and MgO-impregnated clay are listed in Table 2. The second-order response surface polynomial function (Eqs. 11, 12) can be used to predict the dye's optimum operating circumstances:

The assessment of variance (ANOVA) for MG elimination efficiency in the cases of nano-bentonite and MgO-impregnated clay was applied in order to validate the model, as given in Tables 3, 4. The correlation between the variables and the responses was determined using the quadratic model and second-order polynomial analysis. The Model F-values of MG removal percentage achieved by nano-bentonite and MgO-impregnated clay were recorded as 71.81and 36.85, respectively, which were favorable. The model P-values of both models for MG removal were acceptable. Model terms are considered significant when the P-value is less than 0.0500. In this case, A, B, D, AB, AC, AD, BC, and A2 are significant model terms for MgO-impregnated clay. When the value was higher than 0.1, model terms were not considered significant. On the other hand, the model F-value of nano-bentonite was 71.81, indicating that the model was favorable. In this case, A, B, AB, AC, AD, BC, BD, CD, and A2 were satisfied model terms. The lack of fit F-value of nano-bentonite and MgO-impregnated clay were 2.62 and 0.29, respectively, implies the lack of fit is not significant relative to the pure error. There was a 22.64% and 94.48% chance for nano-bentonite and MgO-impregnated clay, respectively that a lack of fit F-value this large could be due to noise. A non-significant lack of fit indicated that the quadratic model was fit for the present study. The second-order polynomial equation was developed based on these findings to indicate a relationship between MG elimination percentage and a number of different variables. Only 0.2% and 0.9% of the total variation could not be explained by the model, according to the regression equation derived after the ANOVA, which indicated that the correlation coefficient (R2) values for the MG dye removal by nano-bentonite and MgO-impregnated clay were 0.986 and 0.973, respectively. A high R2 value (close to1) indicates that the calculated and observed findings within the experimental range are in good agreement with each other, and it also demonstrates that an acceptable and reasonable agreement with adjusted R2. The predicted R2 values for nano-bentonite and MgO-impregnated clay were 0.929 and 0.91, respectively, which are reasonably consistent with the adjusted R2 values: 0.952 and 0.947, respectively. These results demonstrated the effectiveness of the established model and the accuracy and minimal inaccuracy of the independent variable values. Adequate precision is used to determine of the signal to the noise ratio. A ratio larger than 4 is desirable. The values for this ratio were 29.5 and 22.842 for nano-bentonite and MgO-impregnated clay, respectively, indicating the reliability of the experimental data. The repeatability of the model is measured using a parameter called coefficient of variation (CV%), which is the ratio of the standard error of the estimate and the mean value of the observed response (expressed as a percentage).Typically, a model is regarded as replicable if its CV% value is less than 10%54. According to the data listed in Tables 3 and 4, the CV% values of nano-bentonite and MgO-impregnated clay are relatively small, 0.4 and 0.5%, respectively, which indicated that the deviations between experimental and predicted values were low. The plots between experimental (actual) and predicted values of MG removal by RSM model are reported in Fig. 11a,b. Based on this figure, the average differences between the predicted and experimental values can be evinced to be less than 0.1, which indicates that most of the regression model provided an explanation for the data variation.

Linear correlation between experimental and predicted removal efficiency % MG by (a) nano bentonite and (b) MgO impregnated clay.

Three-dimensional surface plots and contour plots were generated to investigate the interaction between MG removal efficiency and two parameters at a time, while the other variables were held at constant values. The data reported in Figs. 12a,b and 13a,b demonstrate unequivocally that, as the temperature increased, so did decolorization percentage along with increasing pH. The maximum removal of MG dye decolorization from 25 to 35 °C, for nano-bentonite and 25–50 °C for MgO-impregnated clay, with increasing pH 7.0 and pH 9.0, there was a rise in the percentage of decolorization, respectively.

3D response surface plot of MG removal % through nano bentonite as a function of pH, temperature and adsorbent dosage.

3D response surface plot of MG removal % through MgO impregnated clay as a function of pH, temperature and adsorbent dosage.

The elliptical shape of the curve is indicative of a high degree of interaction between the three variables. When the interaction of the MG removal efficiency with the adsorbent dosage and the adsorption temperature was examined, it was discovered that this analysis's affecting factor was temperature, as can be evinced from Figs. 12c,d and 13c,d. As the adsorbents’ dosage increased, so did the rate of MG decolorization. The temperature was found to be most influential at an nano-bentonite dosage of 0.2 g/L, in which casea79% decolorization could be observed at 25 °C and 98% decolorization could be observed at 35 °C. Maximum decolorization could be observed at a temperature of 35 °C and adsorbent dosage of 1.0 g/L. On the other hand, maximum decolorization of MG afforded by MgO-impregnated clay could be observed (97%) at a temperature of 50 °C.

The data reported in Figs. 12e,f and 13e,f reflect the effect that the pH and the initial MG concentration had on the percentage of MG removed, in conditions where by the temperature was kept constant. Above a specific initial MG concentration (above 300 mg/L), the adsorption capacity declines as the initial MG concentration increases, but there was a net positive interaction effect, suggesting that the adsorption capacity increases as the initial MG concentration and initial pH increase. The maximum capacities for MG adsorption by nano-bentonite and MgO-impregnated clay were observed at pH values in the 7.0–9.0 range. Thus, evidence indicates that the percentage of noxious dye elimination afforded by nano-bentonite and MgO-impregnated clay was very low at acidic pH 5.0.

Referring back to Figs. 12 and 13, the combined effect on MG removal efficiency of changing the adsorbent dosage and the initial MG concentration were investigated, in conditions where by the temperature and pH were fixed at zero level. As can be evinced from Fig. 12, more than 98% and 90% of the MG dye was removed in the presence of nano-bentonite and MgO-impregnated clay under the mentioned conditions, respectively. Notably, the maximum MG removal percentage was obtained at high adsorbent dosage (0.7 g/L for nano-bentonite) and (1.0 g/L for MgO-impregnated clay), and minimum dye concentration (100 mg/L). As can be evinced from Figs. 12 and 13, dye adsorption decreased as the initial MG concentration increased. This trend may be due to the fixed number of active sites on the adsorbent vis-à-vis an increasing number of dye molecules. Banerjee and Sharma55 reported that the efficiency of dye adsorption on the adsorbents dropped significantly as the initial adsorbate concentration increased.

Kinetic studies on the adsorption of MG onto nano-bentonite and MgO-impregnated clay were conducted by fitting the experimental data with pseudo-1st-order and pseudo-2nd-order reaction rate equations.

The experimental kinetic data were fitted with the Lagergren pseudo-first-order rate equation (Eq. 13)56,57:

where k1 is the pseudo-primary order rate constant (min−1), qe represents the amount of MG removed at time-point t (min) of adsorbent (mg/g), and qt represents the MG adsorption capacity at equilibrium (mg/g). In Fig. 14a,b is reported the plot of log (qe − qt) versus time, whereas the relevant R2 values and constant quantity for such various adsorption kinetic designs are listed in Table 5. Given the discrepancy between the calculated (qe, cal) and experimentally determined (Expqe) adsorption capacities, which can be evinced from Table 5, a pseudo-first-order kinetics model was unable to explain the adsorption of MG onto nano-bentonite and MgO-impregnated clay. Additionally, when compared to the pseudo-second-order value, the values of the coefficient of determination (R2) were relatively small at 0.975 and 0.916, for the nano-bentonite and MgO-impregnated clay cases, respectively.

Pseudo-first order for the adsorption of MG onto (a) nano bentonite and (b) MgO impregnated clay.

The equation for the Lagergren pseudo-second-order kinetics (Eq. 14) is stated linearly as shown below2,57:

where k2 is the pseudo-second-order rate constant of MG adsorption (g/mg/min), and t is the contact time (min). The fitness of the straight line (R2) and the consistency between the experimental and calculated values of qe serve as indicators of each model's validity.

The plot of t/qtversus the contact time is reported in Fig. 15a,b, and the values for the relevant parameters (R2, slope, intercept, pseudo-first order rate constant) "K1", and the experimental and calculated dye uptake levels) are listed in Table 5. As can be evinced from this table, the R2 values for nano-bentonite (0.996) and MgO-impregnated clay (0.999) were quite close to 1. The computed qe values for both nano materials were in excellent agreement with the actual data, when the pseudo-second-order reaction rate equation was utilized for the computation. This observation indicates that the adsorption of MGon nano-bentonite and MgO-impregnated clay proceeds through a mechanism described by a second-order kinetics equation. According to a study conducted by Taher et al.58, the adsorption of the Congored dye onto acid-activated bentonite exhibits pseudo-second-order kinetics.

Pseudo-second order for the adsorption of MG onto (a) nano bentonite and (b) MgO impregnated clay.

The thermodynamic adsorption qualities depend greatly on temperature. The effect of adsorption temperature on the MG adsorption of nano-bentonite and MgO-impregnated clay was investigated at various temperatures (298, 303, 308, 323, and 343 K). During the study on the thermodynamics of dye adsorption, 50 mg/L of dye and 1 g/L of two distinct adsorbents were used at temperatures of 25 °C, 30 °C, 35 °C, 50 °C, and 70 °C.The rate Eq. (15) and the van’t Hoff equation can be used to calculate the thermodynamic parameters, such as changes in the standard free energy (G), enthalpy (H), and entropy (S), related to the adsorption process (16). The rate equation is represented as follows55,59:

Here, ΔG0 is the free energy change of the sorption process (kJ/mol), and KC is the ratio of the equilibrium concentration of the MG ions on the adsorbent to the equilibrium concentration of the MG dye ions in the solution. R is the ideal gas constant (8.314 J/(mol K)),and T is the adsorption temperature in K. After plotting ΔG° against temperature, a linear relationship was achieved. The slope and intercept of the plot were used to compute the values of ΔS° and ΔH°. The results showed that ΔG° calculated from 25 to 70 °C were all negative, indicating that the adsorption of MG solution onto nano-bentonite and MgO-impregnated clay was feasible and spontaneous. Furthermore, analyses of the change inenthalpy (ΔH°) and entropy (ΔS°) were performed using the linear relationship (Eq. 12). Figure 16a,b shows the thermodynamic plot of ΔG° versus T to calculate ΔH° and ΔS°. Table 6 shows that the corresponding ΔH° and ΔS° values for Malachite green adsorption onto nano-bentonite obtained from the intercept and slope of the plot were equal to − 52.68 kJ/mol and − 0.2089 kJ/mol·K, respectively. The negative value of ΔH° in nano-bentonite showed that the adsorption was exothermic and indicated the possibility of chemisorption. These results are consistent with previous reports on the adsorption of MG on AC of rubber seeds, where MG adsorption was a chemisorption process46. The ΔH° and ΔS° values for Malachite green adsorption onto MgO-impregnated clay were 54.6 kJ/mol and 0.19 kJ/mol·K. Furthermore, a positive ΔH° value in MgO-impregnated clay adsorbent activity showed that adsorption was endothermic and suggested the possibility of physisorption. This result corresponds with the findings in the section on the temperature impact, which showed that adsorption capacity increases as temperature rises.

Thermodynamic for the adsorption of MG onto (a) nano bentonite and (b) MgO impregnated clay.

Studies on the adsorption isotherms, such as the Freundlich, Langmuir, and Temkin isotherms, can be used to examine the effectiveness of the adsorbent material used for adsorption. Moreover, they can be used to determine the nature of the interaction between the adsorbed matter and the adsorbent60,61.

According to Ref.15, the Langmuir isotherm model was used to compute the maximal adsorption capacity resulting from complete monolayer coverage on the adsorbent surface and is shown as follows:

Here, qm is the monolayer adsorption capacity (mg/g), qe is the equilibrium adsorption amount of the adsorbate, and Ce (mg/L) is the equilibrium adsorbate concentration. Regarding the adsorption rate (L/mg), KL is the Langmuir isotherm constant. By charting Ce/qe versus Ce, the values of qm and KL at various amounts of nano-bentonite and MgO-impregnated clay can be determined in the range of 0.99 and 1.2 L/mg Fig. 17a,b. A dimensionless constant called the separation factor RL may be used to express the essential properties of a Langmuir isotherm.

Langmuir (a) nano bentonite and (b) MgO impregnated clay plots for adsorption of MG.

Here, RL is the separation term, and Co is the initial concentration of the dye solution (mg/L). The effect of the isotherm shape on “favorable” or “unfavorable” absorptions was considered62. According to the RL values between (0–1), the isotherm is either unfavorable (RL > 1), linearly favorable (RL = 1), and or irreversible (RL = 0). Results from this experiment’s use of nano-bentonite and MgO-impregnated clay were observed for RL between 0.002 and 0.009, indicating that the adsorption was irreversible favorable. Table 7 shows the findings of MG removal on nano-bentonite and MgO-impregnated clay using the Langmuir model. The R2 in Table 7 showed strong positive proof of the adsorption of MG ion adsorbents following the Langmuir isotherm. The suitability of the linear form of the Langmuir model to nano-bentonite was confirmed through the high correlation coefficients R2 > 0.992.Conversely, the linear form of the Langmuir model to MgO-impregnated clay was slightly fit with the regression coefficients (R2) value (0.962%). This shows that the Langmuir isotherm can provide a decent sorption model. Moreover, the adsorption capacities of the nano-bentonite and MgO-impregnated clays were 13.8 and 17.2 mg/g, respectively. This result corresponds with6, who discovered that the adsorption capacity of CuFe2O4 for MG is 22 mg/g.

According to the Freundlich isotherm model, adsorption occurs on a heterogeneous surface with a non-uniform heat distribution over the adsorbent surface. The linearized form of the Freundlich model is given as follows63:

Here, qe is the amount adsorbed per unit mass of the adsorbent, Ce is the equilibrium concentration, and 1/n and Kf are the Frendulich constants. The values of 1/n represent the nonlinearity of the relationship between adsorption and solution concentration. Adsorption is linear if n equals unity, chemical adsorption is implied if the value of n is below unity, and advantageous physical adsorption is implied if n is above unity. Figure 18a,b shows the plots of lnqe versus lnCe for the adsorption of MG dye on nano-bentonite and MgO-impregnated clay. The values of Kf (mg/g) and n are obtained from the intercept and slope, respectively. The values were (1.9 mg/g) and (2.3) for nano-bentonite and (3.6 mg/g) and (1.3) for MgO-impregnated clay. The R2 values for nano-bentonite and MgO-impregnated clay are approximately 0.973% and 0.982%, respectively. This indicates that both systems are favorable and that the MgO-impregnated clay has a higher adsorption capacity. Therefore, the value of 1/n showed the applicability of the adsorbent used over the range of dye solution concentrations that significantly affect the Freundlich adsorption isotherm. The values of n for the MG dye adsorption on nano-bentonite and MgO-impregnated clay were 2.3 g/L and 1.6 g/L, respectively, indicating that the adsorption occurred as a chemical process for n > 1.

Freundlich (a) nano bentonite and (b) MgO impregnated clay plots for adsorption of MG.

The adsorption energy changes and the surface of the adsorbent toward the adsorption of different species in diverse mixes were assessed using the Tempkin adsorption isotherm. The R2 value and decreased error analysis were effective and efficient criteria. The model has typically been used in the following format (Eq. 20):

Here, β = (RT)/b,Tis the absolute temperature in Kelvin, and R is the universal gas constant(8.314 J/(mol K)); the constant β correlates with the heat of adsorption60. As shown in Table 7 and Fig. 19a,b, applying the experimental equilibrium data to Eq. (20) demonstrated excellent and reasonable applicability of the model in explaining and interpreting MG adsorption on nano-bentonite and MgO-impregnated clay. In the Temkin isotherm, positive AT values of 1.4 L/mg and 2.1 L/mg for nano-bentonite and MgO-impregnated clay, respectively, showed that the process was endothermic. The Temkin model also showed a high R2 value, indicating a chemisorption process rather than a physisorption one. The results obtained correspond with those reported by Gündüz60. Furthermore, the R2 values realized using the Tempkin model were similar to those observed using the Langmuir and Freundlich equations.

Temkin (a) nano bentonite and (b) MgO impregnated clay plots for adsorption of MG.

In Table 8, the maximum adsorption capacities (qmax) of nano-bentonite and MgO-impregnated clay for MG adsorption are compared to the qmax of other adsorbents in the literature. The maximum adsorption capacities of MgO-impregnated clay and nano-bentonite for MG are shown to be greater than those of other adsorbent materials, which may be attributed to the strong adsorption capacity of nano-bentonite. Additionally, because the adsorbent surface was negatively charged during the experiment, the electrostatic attraction between positively charged adsorbate species and adsorbent particles grew, which caused additional MG to be adsorbed.

Analyzing the interaction between working factors using conventional methods is challenging. Consequently, predictions of operational factors and their synergistic impact are frequently based on assumptions. Operational factors can be simultaneously and efficiently analyzed, and the degree of interaction can be assessed using RSM. Due to the operational factor screening, the ideal conditions for MG adsorption were determined. The optimum condition of processing factors for MG adsorption was obtained at pH 9,with an initial concentration of 50 mg/L and a 4.0 g/L adsorbent dosage within 35 °C for nano-bentonite. Compared with MgO-impregnated clay, the optimum condition of processing factors was obtained at pH 9, with an initial concentration of 50 mg/L anda4.0 g/L adsorbent dosage within 40 °C. Under these circumstances, the high decolorization efficiency was 97.53% and 93.9% for nano-bentonite and MgO-impregnated clay, respectively.

Supplementary Table 1 shows that the Box–Behnken design with four variables (pH, initial concentration, contact time, and temperature) was used to improve the decolorization process. Supplementary Table 2 shows the experimental and predicted values of the percentage decolorization. The second-order response surface polynomial function allowed the prediction of ideal dye operating conditions. Figure 20a,b shows that the experimental response values for MG decolorization correspond with the predicted response values, the normal probability, and the studentized residual plot.

(a) The actual and predicted values for the decolourization of MG dye by immobilized Mucor sp., (b) normal % probability and (c) the Box–Cox plot.

According to Table 9, the ANOVA results for the quadratic regression model indicated that the model was significant. The superior F value (60.99) and reduced P values (< 0.0500) of Malachite green show that the model terms were significant. The variables A, D, AB, AC, BD, BD, A2, B2, C2, and D2 were determined to be significant model terms for decolorization based on the P values. Furthermore, according to the results of the ANOVA in Supplementary Table 2, the linear effects of the dye temperature, pH, and concentration were found to be increasingly important for MG dye decolorization. According to the “lack of fit F value of 0.715,”the lack of fit was insignificant regarding the pure error. An insignificant lack of fit was regarded as a reliable indicator that the model would be good. The fit of the model was also expressed by the coefficient of regression R2.The predicted R2 of immobilized Mucor sp.was 0.9837, which is consistent with the adjusted R2 of 0.967. These findings indicate that the developed model was satisfactory and that the values of the independent factors were accurate with minimal error. The range of the projected response regarding the associated error was measured with adequate precision. A ratio of at least 4 is acceptable; however, a ratio higher than 4 is preferable. The ratio of 24.1 for Mucor sp. was high, indicating the reliability of the experimental data. Moreover, according to Supplementary Table 2, the coefficient of variation (CV%) values for Mucor sp. obtained in the study are relatively small, with 2.6. This indicated that the deviations between the experimental and predicted values were low. Figure 20c shows a graph of the Box-Cox diagram of model changes in MG removal (%) using Mucor sp. composite determined by a quadratic polynomial. The best lambda value (λ = 1.49) is between the two red vertical lines, so no data transformation is required. The red line shows the minimum (− 0.2900) and maximum (3.32) values, as well as lambdas at 95% confidence interval value.

The biosorption of Malachite green by the fungus was investigated for a pH range of 5–9.

The maximum degree of decolorization (97.8%) was reached at a pH of 7.0, while at a pH of 9, the decolorization rate decreased to 40%. Figure 21a,b shows that the efficacy of dye decolorization using immobilized Mucor sp. decreased with rising pH levels. Moreover, Fig. 21c shows that the removal efficiency was 54% at a pH of 5.0 and 30 °C, and it improved to 87.8% at a pH of 7 and 30 °C. Similar findings were made by Ref.64, who discovered that the efficiency of decolorization of Malachite green using Aspergillus niger was about 97% at a pH of 7.

(a) the cumulative impact of pH and contact time, (b) the cumulative impact of pH and MG dye concentration, (c) the cumulative impact of pH and temperature, (d) the cumulative impact of contact time and MG dye concentration, (e) the cumulative impact of contact time and temperature, (f) the cumulative impact of temperature and MG dye concentration.

Various environmental factors influenced the degradation of Malachite green using Mucor sp. This fungal strain degraded Malachite green effectively from 298 to 303 °C (Fig. 21c,e,f). Figure 21c,e,f shows that the rate of Malachite green decolorization increases as the temperature rises from 25 to 30 °C. Furthermore, Malachite green decolorization by Mucor sp. ON934589.1 reached a maximum of 91.54% at 303 °C. Conversely, as the temperature rose to 313 °C, the decolorization activity decreased (53%) due to the loss of cell viability or inactivation of the decolorizing enzymes65. Arunprasath et al.4 observed that the optimum temperature (30 °C) was the optimum temperature for the decolorization (92%) of Malachite green dye by Lasiodiplodia strains.

The adsorption behavior of MG was studied in concentrations of 5–200 mg/L at a pH of 7.0. In addition, 87.7–97.4% of Malachite green was eliminated by the immobilized fungus at 5–100 mg/L. The decolorization efficiency of Mucor sp. (ON934589.1) fell below 64% when the starting concentration of Malachite green approached 150 mg/L. These findings suggest that high concentrations of Malachite green impede the development of Mucor sp. (ON934589.1). Figure 21b shows the impact of the initial concentration and contact time on the removal of Malachite green dye using immobilized fungus. The immobilized fungus was suppressed at 150 mg/L of Malachite green due to the existence of sulfonic acid on the aromatic ring formed in the medium by the increased concentration of Malachite green, which inhibited the nucleic acid synthesis and microbial cell proliferation66. The findings of this investigation corresponded with those of Ref.67, who found that Aspergillus fumigates immobilized in polyurethane foam had an optimum Malachite green decolorization percentage of about 97.52% (40 mg/L),which reduced to 23% at 70 mg/L.

At the optimum dye concentration (50 mg/L) and biosorbent dosage (6 g/L), the impact of contact time on adsorption was examined from 24 to 72 h. Figure 21a,d shows the influence of contact time on the elimination of the MG dye. The range of the MG’s adsorption efficiency was 18 to 72 h, corresponding to 72% and 97%, respectively. Based on the data, 40 h was determined to be the equilibrium time in the sorption process because no further improvement was observed after reaching maximum adsorption. The high removal efficiency at the beginning of the contact time of 40 h was due to the large surface area available for dye adsorption during the initial stage, and the adsorbent’s capacity gradually depleted over time, as the few remaining vacant surface sites became tough to occupy because of repulsive forces between the solute molecules on the solid and bulk phases68,69. Our results correspond with those of Ref.70, who observed that Lasiodiplodia sp. could decolorize 81% of Malachite green within 36 h.

The Monod model is used to represent the relationship between the limiting substrate concentration and the specific growth rate using Eqs. (19) and (20).

Here, µ, µmax, and Ks were determined as the biodegradation experiment data. The magnitude of Yx/s was estimated from the slope of the graph of dX dt versus S. The original Monod model becomes inadequate when a substrate prevents biodegradation. Monod derivatives with substrate inhibition adjustment Eqs. (24 and 32), suggested by the Haldane, Aiba–Edward, Luong, Han, and Levenspiel models, have been used to assess the impacts of inhibition at a high substrate concentration and stimulation at a low concentration of substrate71,73,74,74. Here, S and μ are the substrate concentration and the specific growth rate, respectively; μmax is the maximum specific growth rate; n and m are experimental constants; Ks is the half substrate saturation coefficient, and Sm is the critical inhibitor concentration (mg/L) above which growth ceases.

Here, µ = specific growth rate of biomass, µmax = maximum consumption rate constant, S = substrate concentration, K1 = the substrate inhibition constant (mg/L), Ks = Monod constant, and Sm = decisive inhibitor concentration (mg/L); n and m are experimental constants.

For the range of concentrations in the study (5–200 mg/L), the length of the lag phase t0 grew exponentially with the Malachite green concentration Supplementary Fig. 1a. Thus, Malachite green was considered to have an inhibiting effect on microbial development at high concentrations. These findings correspond with those previously recorded for mixed cultures36. We compared the evolution of the lag phase to the particular growth rate to gain advanced insight into the impact of the lag phase. Two trends were observed, one below Supplementary Fig. 1a,c and one above Supplementary Fig. 1b the 100 mg/L Malachite green concentration. The time of the lag phase t0 rose linearly with an increase in the maximum specific growth rate when the concentration of Malachite green Supplementary Fig. 1a was less than 100 mg/L. However, a contrary trend was observed for concentrations greater than 100 mg/L supplementary Fig. 1b, where the length of the lag phase t0 increased as the maximum specific growth rate decreased. The findings of the curve fitting Supplementary Fig. 2 using models such as Monod, Luong, Aiba–Edward, Han, and Levenspiel did not match the experimental results and were excluded. The Luong model provided reasonably acceptable results according to software output and visual examination. The accuracy and statistical analyses of the four kinetic models used in the study revealed that Haldane was the most accurate model, having the minimum root-mean-square error and AICc values and the maximum adjusted R2. Table 10 shows the Af and Bf values. The Af and Bf values for Haldane were significant and closest to 1.0.The results of an F-test indicated that the Haldane model was better than the Aiba–Edward, Han, Levenspiel, and Luongmodels, which were 96.1%,92.2%, 84.43%, and 82.2%, respectively. These results indicate that the Haldane model was superior to the rest. The computed values for the Haldane constants in this work, such as the inhibition constant rate symbolized by the maximal growth rate and half-saturation constant umax, Ks, and Ki, were 1.02 h−1, 70 mg/L, and 70 mg/L.

The fungi decolorize MG via biosorption and biodegradation as their main mechanisms. Biosorption occurs immediately as dye molecules bind to the functional groups present on the surface of fungal mycelium, reflected by the rapid decolorization rate, which plateaus once the binding sites are saturated and equilibrium is achieved81. Biodegradation involves enzymatic breakdown of the dyes into smaller molecules. Enzymatic degradation requires a close fit of the polymer chain into the enzyme active site conformational flexibility is necessary for high degradability23. Immobilization of fungal cells may stably maintain the production of various enzymes at levels higher than those achieved with suspended or pellet forms. Moreover, the immobilization of fungal biomass increases fungal resistance to environmental stresses, such as the presence of toxic molecules at high concentrations.Immobilization improves decolorization efficiency of biomass due to less dense fiber packing in comparison with the free fungal biomass. This is because the fungi has a larger surface area available for dye adsorption. The increase in the surface area of fungal biomass tends to reduce the mass transfer limitations, which in turn increases access to pollutant degradation. Immobilization may allow the use of the system repeatedly, allowing easier liquid–solid separation and avoiding clogging phenomena82. The present study has revealed that Mucor sp. composite was able to decolorize 50 mg/L malachite green (87.8%) within 72 h at pH 7.5 and temperature 30 °C were optimized for dye degradation. The most widely researched are white rot fungi, such as Phanerochaete chrysosporium, Bjerkandera sp., Trametes versicolor, Irpex lacteus, and Pleurotus ostreatus, which produce enzymes, such as lignin peroxidase, manganese peroxidase and laccase. They can degrade many aromatic compounds due to their non-specific enzymatic activity83. Reference84 observed that MG dye degradation occurred for 6 days by two fungal strains Aspergillus flavus (99.78%) and Alternaria solani (91.72%), which was up to 10.95 mg/L, when MG was a sole source of carbon. But degradation had increased up 97.43 and 96.91 at 18.25 mg/L%, respectively, when an extra carbon source was added to the medium. As described previously, white-rot fungi are capable of decolorizing dyes significantly,and in most cases, this is due to the activities of lignin peroxidase (LiP)22 and Mn-dependent peroxidase (MnP). Some studies have demonstrated laccase (Lac)-mediated dye decolorization85. Reference63 who reported that the immobilized laccase onto TiO2–ZrO2–SiO2– material degraded Alizarin Red S (ARS), Remazol Brilliant Blue R (RBBR), and Reactive Black 5 (RB5)from an aqueous solution at a concentration 5 mg/L under optimal process conditions, which were pH 5 and 25 °C, with degradation efficiency reached 100%, 91%, and 77%, respectively. In absorption processes, activated carbon is a highly effective and versatile material. MG dye was reported by Ref.86 who showed that they produce an extracellular oxidoreductive, nonspecific, and non-stereo selective enzyme system including lignin peroxidase, tyrosinase, manganese peroxidase, and laccase to destroy MG dye.

The results of the microbial toxicity study demonstrated that the medium containing 100 mg/L (control) MG had inhibition zones, indicating the toxicity of MG to the E. coli and Pseudomonas aeruginose and Staphylococcus aureus strains. The treated sample did not demonstrate any growth inhibition when compared to the untreated 100 mg/L MG, showing that the formation of the adsorption process was nontoxic Supplementary Fig. 3. This suggests that the effluent might not have any negative effects on its surroundings when released into water bodies.

The recyclability of nano-bentonite and MgO-impregnated clay adsorbents for MG removal was studied. Supplementary Fig. 4 shows the results of recycling studies, and the graph shows that there was a minimal loss in MG removal up to seven cycles. However, after seven cycles, the MG removal effectiveness of the nano-bentonite and MgO-impregnated clay declined from 93 to 86.85% and 92.2 to 83%, respectively. Reference68 reported that the reusability of a Curcuma caesia based on the AC adsorbent for the removal of Malachite green was sustained, even after eight cycles at 81%.

This study has shown that nano-bentonite, MgO-impregnated clay, and immobilized Mucor sp. ON934589.1are effective adsorbents for removing MG from aqueous solution. The RSM based on BBD combining was utilized to investigate the effect of four different process variables (adsorbent dosage, initial MG concentration, pH, and contact time) on the dye removal efficiency of nano-bentonite, MgO-impregnated clay, and immobilized Mucor sp. ON934589.1in aqueous solution. The relative effects of the interactions of the mentioned process variables were also successfully analyzed. The corresponding experimental values of dye adsorption were found to be 0.986%, 0.973%, and 0.983%, which extensively corresponded to the optimal values(0.93%, 0.91%, and0.87.8%) predicted by the model RSM for nano-bentonite, MgO-impregnated clay, and Mucor sp. (ON934589.1), respectively. The optimal Malachite green removal efficiency of MgO-impregnated clay was found at a pH of 9.0, an initial MG concentration of 50 ppm, a dosage of 0.7 g, and a contact time of 60 min. However, the Malachite green removal efficiency of nano-clay was observed to be optimal at 35 °C, 7.0, 60 min, 1 g/L, and 50 mg/L. The Malachite green adsorption isotherm on MgO-impregnated clay showed maximum consistency with the Freundlich isotherm model, withan R2 value of 0.982. However, the Langmuir adsorption isotherm was better suited for nano-bentonite (R2 = 0.992). The adsorption activities of nano-bentonite and MgO-impregnated clay were matched to a pseudo-second-order model equation with R2 values of 0.996 and 0.995, respectively. Furthermore, nano-bentonite and MgO-impregnated clay were matched to the Temkin isotherm with R2 values of 0.965 and 0.986, respectively. The Gibbs free energy was positive for nano-clay (0.72–7.5 kJ mol) and negative for MgO-impregnated clay (− 4.07 to − 12.9). Moreover, nano-bentonite and MgO-impregnated clay showed enthalpy changes of − 0.151and 0.196, respectively. A high biodegradation efficiency of 87.8% was obtained during a 72 h decolorization examination of a dye using the isolated fungus Mucor sp. (GenBank accession no. ON934589.1).

All data generated or analyzed during this study are of our own work and it is our pleasure to be available publically. Connect with [email protected].

Asses, N., Farhat, A., Cherif, S., Hamdi, M., Bouallagui, H. Comparative study of sewage sludge co-composting with olive mill wastes or green residues: Process monitoring and agriculture value of the resulting composts (2017).

Puchongkawarin, C., Mattaraj, S. & Umpuch, C. Experimental and modeling studies of methylene blue adsorption onto na-bentonite clay. Eng. Appl. Sci. Res. 48(3), 268–279. https://doi.org/10.14456/easr.2021.29 (2021).

Article Google Scholar

Tarekegn, M. M., Balakrishnan, M. Zerovalent iron, nanoclay and iron impregnated. 30109–30131. https://doi.org/10.1039/d1ra03918k (2021).

Arunprasath, T., Sudalai, S., Meenatchi, R., Jeyavishnu, K. & Arumugam, A. Biocatalysis and Agricultural Biotechnology Biodegradation of triphenylmethane dye malachite green by a newly isolated fungus strain. Biocatal. Agric. Biotechnol. 17(December 2018), 672–679 (2019).

Article Google Scholar

Akpomie, K. G. & Conradie, J. Efficient synthesis of magnetic nanoparticle-Musa acuminata peel composite for the adsorption of anionic dye. Arab. J. Chem. 13(9), 7115–7131. https://doi.org/10.1016/j.arabjc.2020.07.017 (2020).

Article CAS Google Scholar

Vergis, B. R. et al. Removal of malachite green from aqueous solution by magnetic CuFe2O4 nano-adsorbent synthesized by one pot solution combustion method. J. Nanostruct. Chem. 8(1), 1–12. https://doi.org/10.1007/s40097-017-0249-y (2018).

Article CAS Google Scholar

Kabeer, F. A., John, N. & Abdulla, M. H. Biodegradation of malachite green by a newly isolated Bacillus vietnamensis sp. MSB17 from continental slope of the Eastern Arabian Sea: Enzyme analysis, degradation pathway and toxicity studies. Bioremediat. J. 23(4), 334–342. https://doi.org/10.1080/10889868.2019.1671790 (2019).

Article CAS Google Scholar

Sutar, S. S. et al. Biocatalysis and Agricultural Biotechnology Biodegradation and detoxification of malachite green by a newly isolated bioluminescent bacterium Photobacterium leiognathi strain MS under RSM optimized culture conditions. Biocatal. Agric. Biotechnol. 20(May), 101183 (2019).

Article Google Scholar

Omar, H., El-gendy, A. & Al-ahmary, K. Bioremoval of toxic dye by using different marine macroalgae Bioremoval of toxic dye by using different marine macroalgae. Turk. J. Bot. https://doi.org/10.3906/bot-1703-4 (2018).

Article Google Scholar

Ali, I. Phytogenic magnetic nanoparticles functionalized. RSC Adv. https://doi.org/10.1039/c8ra00245b (2018).

Article PubMed PubMed Central Google Scholar

Chaturvedi, V. & Verma, P. Biodegradation of malachite green by a novel copper—Tolerant Ochrobactrum pseudogrignonense strain GGUPV1 isolated from copper mine waste water. Bioresour. Bioprocess. https://doi.org/10.1186/s40643-015-0070-8 (2015).

Article Google Scholar

Yong, L. et al. Photodegradation of malachite green under simulated and natural irradiation: Kinetics, products, and pathways. J. Hazard. Mater. 285, 127–136. https://doi.org/10.1016/j.jhazmat.2014.11.041 (2015).

Article ADS CAS PubMed Google Scholar

Du, J., Zhang, L., Gao, H. & Liao, Y. Removal of methylene blue from aqueous solutions using Poly(AA-co-DVB). J. Dispers. Sci. Technol. 38(10), 1489–1494. https://doi.org/10.1080/01932691.2016.1255955 (2017).

Article CAS Google Scholar

Argumedo-delira, R. & Mario, J. G. Applied sciences trichoderma biomass as an alternative for removal of Congo Red and Malachite green industrial dyes. Appl. Sci. 11, 448 (2021).

Article CAS Google Scholar

Roy, D. C. et al. Isolation and characterization of two bacterial strains from textile effluents having Malachite Green dye degradation ability. bioRxiv https://doi.org/10.1101/2020.03.29.014274 (2020).

Article PubMed PubMed Central Google Scholar

Shamsizadeh, A., Ghaedi, M., Ansari, A., Azizian, S. & Purkait, M. K. Tin oxide nanoparticle loaded on activated carbon as new adsorbent for efficient removal of malachite green-oxalate: Non-linear kinetics and isotherm study. J. Mol. Liq. 195, 212–218 (2014).

Article CAS Google Scholar

Saleh Bashanaini, M. Removal of Malachite green dye from aqueous solution by adsorption using modified and unmodified local agriculture waste. Sci. J. Anal. Chem. 7(2), 42. https://doi.org/10.11648/j.sjac.20190702.12 (2019).

Article CAS Google Scholar

Ermias, M. R. & Aklilu, G. A comparative study on removal of malachite green dye from waste water using different low cost adsorbents. 6(4), 262–266 (2017).

Azmier, M., Nur, A., Afandi, S. & Solomon, O. Optimization of process variables by response surface methodology for malachite green dye removal using lime peel activated carbon. Appl. Water Sci. https://doi.org/10.1007/s13201-015-0284-0 (2017).

Article Google Scholar

Ozturk, D., Sahan, T., Bayram, T., Erkus, A. Application of Response Surface Methodology (RSM) to optimize the adsorption conditions of Cationic Basic Yellow 2 onto pumice samples as a new adsorbent (RSM) to optimize the adsorption conditions of cationic basic yellow 2 onto pumice samples as (2017).

Otavo-loaiza, R. A., Sanabria-gonz, N. R. & Giraldo-g, G. I. Tartrazine removal from aqueous solution by HDTMA-Br-modified colombian bentonite. Sci. World J. 2019, 1–11 (2019).

Article Google Scholar

Jankowska, K. et al. Electrospun biosystems made of nylon 6 and laccase and its application in dyes removal. Environ. Technol. Innov. 21, 101332. https://doi.org/10.1016/j.eti.2020.101332 (2021).

Article CAS Google Scholar

Antecka, K. et al. Synergistic degradation of dye wastewaters using binary or ternary oxide systems with immobilized laccase. Catalysts https://doi.org/10.3390/catal8090402 (2018).

Article Google Scholar

Harouna, M., Tcheka, C. & Dobe, N. Batch equilibrium and kinetic studies of anionic and cationic dyes adsorption onto Al—pillared clay from a local cameroonian clay materials in aqueous medium. Mod. Chem. 8(2), 23–32. https://doi.org/10.11648/j.mc.20200802.12 (2020).

Article CAS Google Scholar

Abegunde, S. M., Idowu, K. S., Adejuwon, O. M. & Adeyemi-Adejolu, T. A review on the influence of chemical modification on the performance of adsorbents. Resour. Environ. Sustain. 1(July), 100001. https://doi.org/10.1016/j.resenv.2020.100001 (2020).

Article Google Scholar

Abdou, M. I. & Dardir, M. M. Evaluation of Egyptian bentonite and nano-bentonite as drilling mud. Egypt. J. Pet. 22(1), 53–59. https://doi.org/10.1016/j.ejpe.2012.07.002 (2013).

Article Google Scholar

Zdravković, A. S., Stanković, N. J., Ristić, N. N. & Petković, G. M. Application of activated bentonite for the removal of direct and reactive dye from aqueous solutions. Chem. Ind. Chem. Eng. Q. 25(4), 341–351. https://doi.org/10.2298/CICEQ171025012Z (2019).

Article Google Scholar

Al-asheh, S. & Banat, F. The removal of methylene blue dye from aqueous solutions using activated and non-activated bentonites. Adsorpt. Sci. Technol. 21, 451–462 (2003).

Article CAS Google Scholar

Tahir, S. S. & Rauf, N. Removal of a cationic dye from aqueous solutions by adsorption onto bentonite clay. Chemosphere 63, 1842–1848. https://doi.org/10.1016/j.chemosphere.2005.10.033 (2006).

Article ADS CAS PubMed Google Scholar

Aichour, A. & Zaghouane, H. Synthesis and characterization of hybrid activated bentonite/alginate composite to improve its effective elimination of dyes stuff from wastewater. Appl. Water Sci. 10(6), 1–3 (2020).

Article ADS Google Scholar

Ahmed, M. A. Mesoporous MgO nanoparticles as a potential sorbent for removal of fast orange and bromophenol blue dyes Mesoporous MgO nanoparticles as a potential sorbent for removal of fast orange and bromophenol blue dyes. Nanotechnol. Environ. Eng. https://doi.org/10.1007/s41204-016-0010-7 (2018).

Article Google Scholar

Thakre, D. et al. Magnesium incorporated bentonite clay for defluoridation of drinking water. J. Hazard. Mater. 180, 122–130. https://doi.org/10.1016/j.jhazmat.2010.04.001 (2010).

Article CAS PubMed Google Scholar

Shah, I., Adnan, R., Saime, W., Ngah, W. & Mohamed, N. Iron impregnated activated carbon as an efficient adsorbent for the removal of iron impregnated activated carbon as an efficient adsorbent for the removal of methylene blue: Regeneration and kinetics studies. PLoS ONE https://doi.org/10.1371/journal.pone.0122603 (2015).

Article PubMed PubMed Central Google Scholar

Fabryanty, R. Removal of crystal violet dye by adsorption using bentonite–alginate composite. J. Environ. Chem. Eng. 5, 5677–5687 (2017).

Article CAS Google Scholar

Kowanga, K. D., Gatebe, E., Mauti, G. O. & Mauti, E. M. Kinetic, sorption isotherms, pseudo-first-order model and pseudo-second-order model studies of Cu (II) and Pb (II) using defatted Moringa oleifera seed powder. J. Phytopharmacol. 5(2), 71–78 (2016).

Article Google Scholar

Uba, G., Abubakar, A. & Ibrahim, S. Optimization of process conditions for effective degradation of Azo blue dye by Streptomyces sp. DJP15: A secondary modelling approach. Bull. Environ. Sci. 5(2), 28–32 (2021).

Google Scholar

Ullah, S. et al. Adsorption of malachite green dye onto mesoporous natural inorganic clays: Their equilibrium isotherm and kinetics studies. Water (Switzerland) https://doi.org/10.3390/w13070965 (2021).

Article PubMed Central Google Scholar

Ourari, A., Tennah, F., Ruíz-Rosas, R., Aggoun, D. & Morallón, E. Bentonite modified carbon paste electrode as a selective electrochemical sensor for the detection of Cadmium and Lead in aqueous solution. Int. J. Electrochem. Sci. 13(2), 1683–1699. https://doi.org/10.20964/2018.02.35 (2018).

Article CAS Google Scholar

Shan, T. C., Al Matar, M., Makky, E. A. & Ali, E. N. The use of Moringa oleifera seed as a natural coagulant for wastewater treatment and heavy metals removal. Appl. Water Sci. 7(3), 1369–1376. https://doi.org/10.1007/s13201-016-0499-8 (2017).

Article ADS CAS Google Scholar

Akoremale, E. & Olaseni, O. K. S. Comparative studies on the adsorption of rhodamine B and malachite green from simulated wastewater onto bentonite clay. ChemSearch J. 10(2), 30–40 (2019).

Google Scholar

Blanco-Flores, A., Colín-Cruz, A., Gutiérrez-Segura, E. & Vilchis-Nestor, A. Removal of malachite green dye from aqueous solution through inexpensive and easily available tuffite, bentonite and vitreous tuff minerals. Rev. Latinoam. Recur. Nat. 12(1), 1–17 (2016).

Google Scholar

Zhirong, L., Azhar Uddin, M. & Zhanxue, S. FT-IR and XRD analysis of natural Na-bentonite and Cu(II)-loaded Na-bentonite. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 79(5), 1013–1016. https://doi.org/10.1016/j.saa.2011.04.013 (2011).

Article ADS CAS Google Scholar

Tastan, B. E., Özdemir, C. & Tekinay, T. Effects of different culture media on biodegradation of triclosan by Rhodotorula mucilaginosa and Penicillium sp. Water Sci. Technol. 74(2), 473–481. https://doi.org/10.2166/wst.2016.221 (2016).

Article CAS Google Scholar

Popli, S. & Patel, U. D. Destruction of azo dyes by anaerobic–aerobic sequential biological treatment: A review. Int. J. Environ. Sci. Technol. 12(1), 405–420. https://doi.org/10.1007/s13762-014-0499-x (2015).

Article CAS Google Scholar

Chen, J. et al. “Comparative study on the fungicidal activity of metallic MgO nanoparticles and macroscale MgO against soilborne fungal phytopathogens. Front. Microbiol. 11, 1–19. https://doi.org/10.3389/fmicb.2020.00365 (2020).

Article Google Scholar

Chieng, H. I., Lim, L. B. L. & Priyantha, N. Enhancing adsorption capacity of toxic malachite green dye through chemically modified breadnut peel: Equilibrium, thermodynamics, kinetics and regeneration studies. Environ. Technol. (U.K.) 36(1), 86–97. https://doi.org/10.1080/09593330.2014.938124 (2015).

Article CAS Google Scholar

Ashiq, A. et al. Municipal solid waste biochar-bentonite composite for the removal of antibiotic ciprofloxacin from aqueous media. J. Environ. Manag. 236(February), 428–435. https://doi.org/10.1016/j.jenvman.2019.02.006 (2019).

Article CAS Google Scholar

Jinendra, U., Nagabhushana, B. M. & Bilehal, D. Comparative adsorptive and kinetic study on the removal of malachite green in aqueous solution using titanium coated graphite and titanium coated graphite with cnt-abs nanocomposite. Desalin. Water Treat. 209, 392–401. https://doi.org/10.5004/dwt.2021.26536 (2021).

Article CAS Google Scholar

Auta, M. & Hameed, B. H. Modified mesoporous clay adsorbent for adsorption isotherm and kinetics of methylene blue. Chem. Eng. J. 198–199, 219–227. https://doi.org/10.1016/j.cej.2012.05.075 (2012).

Article CAS Google Scholar

Bao, Y. & Zhang, G. Study of adsorption characteristics of methylene blue onto activated carbon made by Salix psammophila. Energy Proc. 16(PART B), 1141–1146. https://doi.org/10.1016/j.egypro.2012.01.182 (2012).

Article CAS Google Scholar

Yao, S. et al. Occurrence and removal of antibiotics, antibiotic resistance genes, and bacterial communities in hospital wastewater. Environ. Sci. Pollut. Res. 28(40), 57321–57333. https://doi.org/10.1007/s11356-021-14735-3 (2021).

Article CAS Google Scholar

Kuang, Y., Zhang, X. & Zhou, S. Adsorption of methylene blue in water onto activated carbon by surfactant modification. Water 12, 1–19 (2020).

Article ADS Google Scholar

Mortazavi, K., Rajabi, H., Ansari, A., Ghaedi, M. & Dashtian, K. Preparation of silver nanoparticle loaded on activated carbon and its application for removal of malachite green from aqueous solution. Synth. React. Inorg. Metal-Org. Nano-Metal Chem. https://doi.org/10.1080/15533174.2016.1228670 (2016).

Article Google Scholar

Owolabi, R. U., Usman, M. A. & Kehinde, A. J. Modelling and optimization of process variables for the solution polymerization of styrene using response surface methodology. J. King Saud Univ. Eng. Sci. 30(1), 22–30. https://doi.org/10.1016/j.jksues.2015.12.005 (2018).

Article Google Scholar

Banerjee, S. & Sharma, Y. C. Equilibrium and kinetic studies for removal of malachite green from aqueous solution by a low cost activated carbon. J. Ind. Eng. Chem. 19, 1099–1105 (2013).

Article Google Scholar

Abou-gamra, Z. M. & Ahmed, M. A. TiO 2 nanoparticles for removal of malachite green dye from waste water. Adv. Chem. Eng. Sci. 5, 373–388 (2015).

Article CAS Google Scholar

Ho, Y. S. & McKay, G. Pseudo-second order model for sorption processes. Process Biochem. 34(5), 451–465. https://doi.org/10.1016/S0032-9592(98)00112-5 (1999).

Article CAS Google Scholar

Taher, T., Rohendi, D., Mohadi, R. & Lesbani, A. Congo red dye removal from aqueous solution by acid-activated bentonite from sarolangun: Kinetic, equilibrium, and thermodynamic studies. Arab J. Basic Appl. Sci. https://doi.org/10.1080/25765299.2019.1576274 (2019).

Article Google Scholar

Muinde, V. M., Onyari, J. M., Wamalwa, B., Wabomba, J. & Nthumbi, R. M. Adsorption of malachite green from aqueous solutions onto rice husks: Kinetic and equilibrium studies. J. Environ. Prot. https://doi.org/10.4236/jep.2017.83017 (2017).

Article Google Scholar

Gündüz, F. & Bayrak, B. Biosorption of malachite green from an aqueous solution using pomegranate peel: Equilibrium modelling, kinetic and thermodynamic studies. J. Mol. Liq. 243, 790–798. https://doi.org/10.1016/j.molliq.2017.08.095 (2017).

Article CAS Google Scholar

Gündüz, F. PT. J. Mol. Liq. https://doi.org/10.1016/j.molliq.2017.08.095 (2017).

Article Google Scholar

Kushwaha, A. K., Gupta, N. & Chattopadhyaya, M. C. Removal of cationic methylene blue and malachite green dyes from aqueous solution by waste materials of Daucus carota. J. Saudi Chem. Soc. https://doi.org/10.1016/j.jscs.2011.06.011 (2011).

Article Google Scholar

Archana, S. et al. Numerical investigations of response surface methodology for organic dye adsorption onto Mg-Al LDH-GO Nano Hybrid: An optimization, kinetics and isothermal studies. J. Indian Chem. Soc. 99(1), 100249. https://doi.org/10.1016/j.jics.2021.100249 (2022).

Article CAS Google Scholar

Alam, M. Z., Khan, M. J. H., Kabbashi, N. A. & Sayem, S. M. A. Development of an effective biosorbent by fungal immobilization technique for removal of dyes. Waste Biomass Valoriz. 9(4), 681–690. https://doi.org/10.1007/s12649-016-9821-9 (2018).

Article CAS Google Scholar

Afrin, S. et al. The degradation of textile industry dyes using the effective bacterial consortium. Heliyon 7(10), e08102. https://doi.org/10.1016/j.heliyon.2021.e08102 (2021).

Article CAS PubMed PubMed Central Google Scholar

Barapatre, A., Aadil, K. R. & Jha, H. Biodegradation of malachite green by the ligninolytic fungus Aspergillus flavus. Clean: Soil, Air, Water 45(4), 1–12. https://doi.org/10.1002/clen.201600045 (2017).

Article CAS Google Scholar

Ghany, T., Abboud, M., Alawlaqi, M. & Shater, A. Dead biomass of thermophilic Aspergillus fumigatus for Congo red biosorption. Egypt. J. Exp. Biol. 15(1), 1. https://doi.org/10.5455/egyjebb.20181206084342 (2019).

Article Google Scholar

Arora, C. et al. Efficient removal of malachite green dye from aqueous solution using curcuma caesia based activated carbon. Desalin. Water Treat. 195, 341–352. https://doi.org/10.5004/dwt.2020.25897 (2020).

Article CAS Google Scholar

Kumar, P. S., Sivaprakash, S. & Jayakumar, N. Removal of Methylene Blue dye from aqueous solutions using Lagerstroemia indica seed (LIS) activated carbon. Int. J. Mater. Sci. 12(1), 107–116 (2017).

Google Scholar

Arunprasath, T., Sudalai, S., Meenatchi, R., Jeyavishnu, K. & Arumugam, A. Biodegradation of triphenylmethane dye malachite green by a newly isolated fungus strain. Biocatal. Agric. Biotechnol. 17, 672–679. https://doi.org/10.1016/j.bcab.2019.01.030 (2019).

Article Google Scholar

Basu, S., Dasgupta, M. & Chakraborty, B. Removal of Chromium (VI) by Bacillus subtilis isolated from East Calcutta Wetlands, West Bengal, India. Int. J. Biosci. Biochem. Bioinform. 4(1), 7–10. https://doi.org/10.7763/ijbbb.2014.v4.300 (2014).

Article CAS Google Scholar

Johari, M. S. Mathematical modeling of the growth kinetics of Bacillus sp. on Tannery effluent containing chromate. J. Environ. Bioremed. Toxicol. 2(1), 6–10 (2014).

Article Google Scholar

Hamitouche, A. E., Bendjama, Z., Amrane, A., Kaouah, F. & Hamane, D. Relevance of the Luong model to describe the biodegradation of phenol by mixed culture in a batch reactor. Ann. Microbiol. 62(2), 581–586. https://doi.org/10.1007/s13213-011-0294-6 (2012).

Article CAS Google Scholar

Han, K. & Levenspie, O. Extended monod kinetics for substrate, product, and cell inhibition. Biotechnol. Bioeng. 32, 430–437 (1988).

Article CAS PubMed Google Scholar

Garg, V. K., Kumar, R. & Gupta, R. Removal of malachite green dye from aqueous solution by adsorption using agro-industry waste: a case study of Prosopis cineraria. Dyes Pigm. 62(1), 1–10 (2004).

Article CAS Google Scholar

Mohammadi, A., Daemi, H. & Barikani, M. Fast removal of malachite green dye using novel superparamagnetic sodium alginate-coated Fe3O4 nanoparticles. Int. J. Biol. Macromol. 69, 447–455 (2014).

Article CAS PubMed Google Scholar

Sundararaman, T. R. et al. Adsorptive removal of malachite green dye onto coal-associated soil and conditions optimization. Adsorp. Sci. Technol. 2021, 1–11 (2021).

Google Scholar

Chowdhury, S. & Saha, P. Sea shell powder as a new adsorbent to remove basic green 4 (malachite green) from aqueous solutions: equilibrium, kinetic and thermodynamic studies. Chem. Eng. J. 164, 168–177 (2010).

Article CAS Google Scholar

El-Zahhar, A. A. & Awwad, N. S. Removal of malachite green dye from aqueous solutions using organically modified hydroxyapatite. J. Environ. Chem. Eng. 4(1), 633–638 (2016).

Article CAS Google Scholar

Geetha, P., Latha, M. & Koshy, M. Biosorption of malachite green dye from aqueous solution by calcium alginate nanoparticles: equilibrium study. J. Mol. Liq. 212, 723–730 (2015).

Article CAS Google Scholar

Marcharchand, S. & Ting, A. S. Y. Trichoderma asperellum cultured in reduced concentrations of synthetic medium retained dye decolourization efficacy. J. Environ. Manag. 203, 542–549. https://doi.org/10.1016/j.jenvman.2017.06.068 (2017).

Article CAS Google Scholar

Toh, Y. C., Lin Yen, J. J., Obbard, J. P. & Ting, Y. P. Decolourisation of azo dyes by white-rot fungi (WRF) isolated in Singapore. Enzyme Microb. Technol. 33(5), 569–575. https://doi.org/10.1016/S0141-0229(03)00177-7 (2003).

Article CAS Google Scholar

Przystaś, W., Zabłocka-Godlewska, E. & Grabińska-Sota, E. Efficiency of decolorization of different dyes using fungal biomass immobilized on different solid supports. Braz. J. Microbiol. 49(2), 285–295. https://doi.org/10.1016/j.bjm.2017.06.010 (2018).

Article CAS PubMed Google Scholar

Ali, H., Ahmad, W., Haq, T. Decolorization and degradation of malachite green by Aspergillus flavus and Alternaria solani. (2010).

Sumathi, S. & Manju, B. S. Uptake of reactive textile dyes by Aspergillus foetidus. Enzyme Microb. Technol. 27(6), 347–355. https://doi.org/10.1016/S0141-0229(00)00234-9 (2000).

Article CAS PubMed Google Scholar

Shanmugam, V., Manoharan, S., Sharafali, A., Anandan, S. & Murugan, R. Green grasses as light harvesters in dye sensitized solar cells. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 135, 947–952. https://doi.org/10.1016/j.saa.2014.07.096 (2015).

Article ADS CAS Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Central Laboratory for Environmental Quality Monitoring, National Water Research Center, Shubra El Kheima 1, Al Qalyubia Governorate, 6210001, Egypt

Mohammed Taha Moustafa

You can also search for this author in PubMed Google Scholar

M.T.M.: provided conception and design of research; acquisition, analysis, and interpretation of data; drafted the manuscript and substantively revised it and processed creation of new software used in the research, and revised the manuscript. The authors read and approved the final manuscript. All authors consent to publishing the manuscript in Scientific Reports.

Correspondence to Mohammed Taha Moustafa.

The author declares no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Moustafa, M.T. Preparation and characterization of low-cost adsorbents for the efficient removal of malachite green using response surface modeling and reusability studies. Sci Rep 13, 4493 (2023). https://doi.org/10.1038/s41598-023-31391-4

Download citation

Received: 02 December 2022

Accepted: 10 March 2023

Published: 18 March 2023

DOI: https://doi.org/10.1038/s41598-023-31391-4

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.